| Mofuta oa Lekhetho: | T/T,Paypal |
| Incoterm: | FOB,CFR,CIF,EXW,DDU |
| Min. Laela: | 1 Piece/Pieces |
| Lipalangoang: | Ocean,Land,Air,Express,Others |
| Port: | Shenzhen,Guangzhou,Hongkong |
Setšoantšo sa No.: HONYFR4-Washer
Mochine: Hony
| Ho rekisa lihlopha | : | Piece/Pieces |
| Mofuta oa Sephutheloana | : | Kantle lebone |
The file is encrypted. Please fill in the following information to continue accessing it
Khalase ea Insular FR4 / G10 Ission Khalase ea Epoloy ea Epoloxy , le leqephe la li-fiberglass, e tsejoang ka li-epoxe tsa khalase ka mocheso le khatello. E na le khatello e phahameng ea mocheso, ho na le matla a phomolo a mala a ho khutlela malapeng, li-ul94-V0, thepa e phahameng haholo, boleng bo botle ba hae, bo boreleli, jj.
Mofuta oa Lihlahisoa: Epoxy Fiberglass Laminate Filimi ea Laminate
Lintho tse bonahalang: Sefate sa Retheme sa Epoxe +
Likarolo tsa sehlooho
1) Seterata sa ho khutla.
2) ho hanyetsa.
3) ho hanyetsa ha mongobo.
4) Ho hanyetsa mocheso mocheso.
5) Khanyetso ea mocheso: 150-180
6) Borati bo botle, bo boreleli, ha bo na likoti.
Kopo
Ka tatellano ea mochini e nang le motlakase
E sebelisoang ho tlhokahalo ea Inthanete ea Motlakase.
Likarolo tsa mochini oa lik'hemik'hale
Likarolo tsa General Mechini le GAR, Generator, Mads, Base, Baffle
Generetor, e leng se fetohang, lebone, sejo se majabajaba.
|
Item
|
Value
|
||
|
Specific gravity
|
G/cm & sup3;
|
1,70 ~ 1,90
|
|
|
° C
|
155
|
||
|
Bending strength min
|
Longitudinal
|
MPA 343,2
|
|
|
Cross
|
MPA 284,4
|
||
|
Tensile strength min
|
Longitudinal
|
MPA 294,2
|
|
|
Cross
|
KJ/sqm 147,1
KJ/sqm 98,1 |
||
|
Impact resistance min
|
Cross
Longitudinal |
KJ/sqm 147,1
KJ/sqm 98,1 |
|
|
Surface resistance min
|
Under normal condition
After immersion in water |
Ohm
|
Ω 1x1013
Ω 1x1011 |
|
Volume resistance min
|
Under normal condition
After immersion in water |
Ohm cm
|
Ω cm 1x1013
Ω cm 1x1011 |
|
Insulation Resistance parallel
To laminate ionmin |
Under normal condition
After immersion in water |
Ohm
|
Ω 1x1010
Ω 1x108 |
|
Dielectric loss Max
|
50Hz
|
KV/mm 0,05
|
|
|
Impact strength
Perpendicular to sheets (At 90 ± 2 ° C in transformer oil) Min |
Thick 0,5 ~ 1mm
|
KV/mm 22,0
|
|
|
Thick 0,5 ~ 1mm
|
KV/mm 20,0
|
||
|
Thick 0,5 ~ 1mm
|
KV/mm 18,0
|
||
|
Leaf with thick more than 3mm will be edited up to 3mm from one side
|
KV/mm 18,0
|
||
|
Breakdown voltage parallel to sheets
(At 90 ± 2 ° C in transformer oil) |
Min
|
KV
|
30,0
|
FR-4 Fiber Gloss Plas polasetiki e lutseng, khalase ea polasetiki ea polasetiki
1. khatello e phahameng le khatello e chesang.
2) sehlopha se futhumetseng: sehlopha sa B.
3) Bophahamo: 0,2-50mmmm
4) Boholo: bophara / bolelele (mm) 1020 * 2040m, 1020 * 1200mm
5) Mmala: Green / Ntšo
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Tlatsa tlhaiso-leseling e eketsehileng e le hore e ka ikopanya le uena kapele
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Contact Now