Setšoantšo sa No.: TECAST® T EF natural PA 6 C Bio-based
Mochine: TEcast
| Ho rekisa lihlopha | : | Kilogram |
| Mofuta oa Sephutheloana | : | Sephutheloana sa kantle ho naha |
The file is encrypted. Please fill in the following information to continue accessing it
Tiala oa tlhaho (Bio-Pa) ke mefuta e meng e botsoalle ea tikoloho ea nylon ea ho il'o etsa lintho tse ikemetseng ea thabo, e le karolo ea tharollo ea rona e tsitsitseng.
Sepothotho se thehiloeng ho Bio se Thehiloeng ke polyamide (pa6c) le se nang le lintlha tse lekaneng tse lekaneng. Ka hona, e na le bolo ea maoto ea cO2 e fokotsehileng ha e bapisoa le mofuta oa Fossil.
Mabapi le thepa, bioplays e lekantsoeng ka bongata e bapisoa le mofuta oa mafura a fossil, 'me e tšoantšitsoe ka ho khetheha thepa e ntle ea mochini, hammoho le thepa e ntle haholo. Li-Pa6s Bioplatic hangata li sebelisoa e le thepa e ntle bakeng sa litebele ka lebaka la eona le bohloko, hape e tla re thusa ho fumana melemo.
E fepa e hlahisa moatlelli, Biopolymer Teaicast T Ef In
TECANDA TP IT IF IFE ke karolo ea "Rece of Papali ea Dading" e kenyelletsa lihlahisoa tse ekelang ka hloko ts'ireletso ea maoto ea tikoloho.
Lintlha
Booksication ea lik'hemik'hale
PA 6 C (a lahletse leqephe la 6)
Mmala
Ivory
Letsoalo
1.15 g / cm3
Likarolo tsa sehlooho
ho tsoa ho lisebelisoa tse thehiloeng ho bio-ext
e kopantsoe hantle
Slide e ntle le ho roala thepa
ho hlohlona ka motlakase
matla a phahameng
Litsela tse monate
ho hanyetsa oli e mengata, mafura le li-huels
ho ba thata haholo
Liindasteri tse Tsoang
boenjineri ba mechini
theknoloji ya lijo
indasteri ea oli le khase
Indasteri ea likoloi
Indasteri e boima ea mosebetsi
TABANE T E E E E E-TOCHING TECION TEMA TODSION TEMPION
| Mechanical properties | ||||
| Mechanical properties | Value | Unit | Parameter | Norm |
| Modulus of elasticity | 3500 | MPa | 1mm/min | DIN EN ISO 527-2 |
| (tensile test) | ||||
| Tensile strength | 83 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 80 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield (tensile test) | 4 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break (tensile test) | 40 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 109 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity | 3200 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| (flexural test) | ||||
| Compression modulus | 2900 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Compression strength | 19/36/83 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 4 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Shore hardness | 83 | D | DIN EN ISO 868 | |
| Thermal properties | ||||
| Thermal properties | Value | Unit | Parameter | Norm |
| Glass transition temperature | 40 | C | DIN EN ISO 11357 | |
| Melting temperature | 215 | C | DIN EN ISO 11357 | |
| Heat distortion temperature | C | HDT, Method A | ISO-R 75 Method A | |
| Thermal conductivity | 0.38 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.7 | J/(g*K) | ISO 22007-4:2008 | |
| Service temperature | 170 | C | short term | NN |
| Service temperature | 100 | C | long term | NN |
| Thermal expansion (CLTE) | 12 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 12 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Electrical properties | ||||
| Electrical properties | Value | Unit | Parameter | Norm |
| surface resistivity | 1014 | Ω | DIN IEC 60093 | |
| volume resistivity | 1014 | Ω*cm | DIN IEC 60093 | |
| Dielectric strength | kV/mm | DIN 53483-1 | ||
| Other properties | ||||
| Other properties | Value | Unit | Parameter | Norm |
| Resistance to hot water/ bases | (+) | - | - | |
| Flammability (UL94) | HB | - | corresponding to | DIN IEC 60695-11-10; |
| Resistance to weathering | - | - | - | |
| Water absorption | 0.2 - 0.4 | % | 24h / 96h (23°C) | DIN EN ISO 62 |
| Water absorption | % | saturation (23°C) | DIN EN ISO 62 | |
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Tlatsa tlhaiso-leseling e eketsehileng e le hore e ka ikopanya le uena kapele
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Contact Now