Setšoantšo sa No.: TECAMID 66 natural PA 66 UNFILLED
Mochine: Tekamid
| Ho rekisa lihlopha | : | Kilogram |
| Mofuta oa Sephutheloana | : | Sephutheloana sa kantle ho naha |
The file is encrypted. Please fill in the following information to continue accessing it
Polyamide 66 e na le thata e ntle, ho thata, ho hanyetsa ab e khahlanong le thibelo ea absaa le ho tsitsipaola ka ho fetisisa. Ntle le moo, nylon 66 e ikhethile ka ho hanyetsa le thepa e tlase ea likhomo. E boetse e na le mocheso o motle haholo, lik'hemik'hale le mekhoa ea ho ama. Basebelisi ba lokela ho hlokomela mokhoa oa PA 66 ho monya mongobo o ka amang botsitso bo boholo. Ebile, PA 66 e tla amohela mongobo o mongata oa ho hlonepha ho tsoa likopanong tsa motlakase, ho hloma liahelo, kaho.
Lintlha
Booksication ea lik'hemik'hale
Pa 66 (polyamide 66)
Mmala
Ivory
Letsoalo
1.15 g / cm3
Likarolo tsa sehlooho
Slide e ntle le ho roala thepa
ho hlohlona ka motlakase
Litsela tse monate
e ntle e holofetseng ebile e kandable
matla a phahameng
ho hanyetsa oli e mengata, mafura le li-huels
ho ba thata haholo
Liindasteri tse Tsoang
boenjineri ba mechini
theknoloji ya lijo
Lisebelisoa tsa motlakase
Thepa ea sefofane le Aerospace
Indasteri ea likoloi
Tekamid 66 Natural PA 66 E sa hlalosoang ea Mahlale a data a sa sebetseng
| Mechanical Properties | ||||
| VALUE | UNIT | PARAMETER | NORM | |
| Modulus of elasticity | 3500 | MPa | 1mm/min | DIN EN ISO 527-2 |
| (tensile test) | ||||
| Tensile strength | 85 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 84 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield (tensile test) | 7 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break (tensile test) | 70 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 110 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity | 3100 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| (flexural test) | ||||
| Compression modulus | 2700 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 5 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 175 | MPa | ISO 2039-1 | |
| Compression strength | 20/35/81 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Thermal Prpperties | ||||
| ROPERTIES | VALUE | UNIT | PARAMETER | NORM |
| Glass transition temperature | 47 | C | DIN EN ISO 11357 | |
| Melting temperature | 258 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.36 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1.5 | J/(g*K) | ISO 22007-4:2008 | |
| Service temperature | 170 | C | short term | NN |
| Service temperature | 100 | C | long term | NN |
| Thermal expansion (CLTE) | 11 | 10-5*1/K | 23-60℃, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 12 | 10-5*1/K | 23-100℃, long. | DIN EN ISO 11359-1;2 |
| Electrical Properties | ||||
| ROPERTIES | VALUE | UNIT | PARAMETER | NORM |
| surface resistivity | 1014 | Ω | - | |
| volume resistivity | 1014 | Ω | ||
| Other Properties | ||||
| VALUE | UNIT | PARAMETER | NORM | |
| Resistance to hot water/ bases | (+) | - | - | |
| Flammability (UL94) | HB | - | corresponding to | DIN IEC 60695-11-10; |
| Resistance to weathering | - | - | - | |
| Water absorption | 0.2 - 0.4 | % | 24h / 96h (23°C) | DIN EN ISO 62 |
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Tlatsa tlhaiso-leseling e eketsehileng e le hore e ka ikopanya le uena kapele
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Contact Now