Setšoantšo sa No.: Ceramic filled PEEK TECAPEEK CMF grey
Mochine: Tecapeek
| Ho rekisa lihlopha | : | Kilogram |
| Mofuta oa Sephutheloana | : | Sephutheloana sa kantle ho naha |
The file is encrypted. Please fill in the following information to continue accessing it
Tecapeek Cmf Grey ke lisebelisoa tse kopaneng tse thehiloeng ho VicTRex® Peek 450g Polymer, e tlatsitsoeng ka pigment ea lehola le e putsoa. Mofuta oa Tecapeek cmf ke mefuta e fapaneng ea mebala le thepa e tšoeu, ka hona e loketse lits'ebetso tsa meaho, kapa bakeng sa lits'ebetso tsa 'mala o moputsoa o tsejoa.
Letoto la tecapeek Cli le 'nile la etsetsoa li-fililer tsa ceramic ho fana ka boemo bo tsitsitseng ba ho tsitsa le ho mamella ka tsela e nepahetseng ea ho fana ka lisekoerethi ea tlhahlobo le litlolo tsa elektroniki.
Ts'ebetso ea Ceramic e lumellang ho nepahala e phahameng le boholo ba likarolo tse nepahetseng ka ho hanela sebōpeho le mekhabiso nakong ea ho tsamaisa mechining, hammoho le ho fokotsa mongobo. Ho fokotsa tlhokahalo ea ts'ebetso ea bobeli ea bohlasoa e theola litšenyehelo tsa masela. Boemo bo nepahetseng ba ho satalla le melala e lumella mechini ea meno a li-micro tse nyane ho feta 0,1 ka boemo ba hole bo phahameng.
Boemo bo phahameng ba ho tsitsa bo boetse bo thusa motho hore a hanele ho khumama likarolo ka likarolo tse tšesaane. Testaek Cmf e boloka litšobotsi tse ikhethang tsa tlhaho tse haufi tse kang mocheso o phahameng oa khatello ea mocheso, ke tokollo e tlase ea meutloa le matla a mangata.
Ha ho bapisoa le lithota tsa fiber-tse matlafalitsoeng, peeramati ea peerachini e ileng ea fokotsa ho fokotseha ha motho e mong, ho nolofatsa boemo bo phahameng ba hole. Fokotsa ho roala hanyane ha ho bapitoe le bana ba lipalesa tse matlafalitsoeng, ho na le litšenyehelo tsa ho taka. Lehlale le nang le lijana tse entsoeng ka ente, TarApeek cmF e hlahisoa hanyane ka hanyane likhatello tse sa feleng, ntoa ea ntoa le lia koba nakong ea ho beoa. Khatello e tlase ea kahare le 'maraka o bohlokoa bakeng sa ho lemoha manyala a likhoele tsa marang-rang a nang le thepa e tšesaane ea sefapano. Ho feta moo, khatello e tlase ea kahare e thusa ho potlaka ka lebelo le ho fepa ka mokhoa o potlakileng nakong ea tlhahiso le chai e fokotsa litšenyehelo tsa masela le nako.
Tecapeek Cmf Grey e kenyelelitsoe sepakapakeng sa Semicouctor sa Eicoudio, se hlahisoang ka taolo e tiileng ea litšila le ho fana ka koto ea kopo. Ka tsela ena, e fepa e tiisa boemo bo phahameng ka ho fetisisa ba bohloeki le ts'ebetso ea boleng bo sa feleng ba Profaele ea thepa ena e ikhethang. Ka tecapeek SD e ntšo, e fepa le eona e fana ka mofuta oa esd o nang le thepa e ts'oanang e nang le matla a ho ntlafatsa.
Joalo ka lisebelisoa tsohle tsa sehlopha sa semiconductor, re ka netefatsa hore mefokolo ea Tekate ea Tecapeek Cmf
Lintlha
Booksication ea lik'hemik'hale
Peek (Polyetherechanetone)
Mmala
Grey
Mebala e meng e fumanehang
tšoeu
Letsoalo
1.65 g / cm3
Likarolo tsa sehlooho
Mechine e metle
matla a phahameng
ho satalla ha phahameng
Katoloso e tlase ea mocheso
Lower Burring
mocheso o motle oa mocheso
botsitso bo botle haholo ba futhumatsang
Liindasteri tse Tsoang
Semiconductor theknoloji
boenjineri ba mechini
Mahlale a Xuum
Lisebelisoa tsa motlakase
Leqephe la data la Mahlale
| Modulus of elasticity | 5500 | MPa | 1mm/min | DIN EN ISO 527-2 |
| (tensile test) | ||||
| Tensile strength | 105 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 102 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield (tensile test) | 4 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break (tensile test) | 5 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 170 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity | 5500 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| (flexural test) | ||||
| Compression modulus | 4300 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | 35 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Ball indentation hardness | 286 | MPa | ISO 2039-1 | |
| Compression strength | 25/46/105 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Glass transition temperature | 151 | C | DIN EN ISO 11357 | |
| Melting temperature | 339 | C | DIN EN ISO 11357 | |
| Thermal conductivity | 0.38 | W/(k*m) | ISO 22007-4:2008 | |
| Specific heat | 1 | J/(g*K) | ISO 22007-4:2008 | |
| Service temperature | 300 | C | short term | NN |
| Service temperature | 260 | C | long term | NN |
| Thermal expansion (CLTE) | 5 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 5 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 6 | 10-5*1/K | 100-150°C, long. | DIN EN ISO 11359-1;2 |
| surface resistivity | 1014 | Ω | - | |
| volume resistivity | 1014 | Ω*cm | ||
| Resistance to hot water/ bases | + | - | - | |
| Flammability (UL94) | V0 | - | corresponding to | DIN IEC 60695-11-10; |
| Resistance to weathering | - | - | - | |
| Water absorption | 0.02 - 0.03 | % | 24h / 96h (23°C) | DIN EN ISO 62 |
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Tlatsa tlhaiso-leseling e eketsehileng e le hore e ka ikopanya le uena kapele
Polelo ea boinotšing: Lekunutu la hau le bohlokoa haholo ho rona. Khamphani ea rona e tšepisa hore ha e etse hore u se ke ua senola tlhahisoleseling ea hau ho ea pele.
Contact Now